Dissolved oxygen (DO) and pH value of leachate, radioactivity, and mortality and molecular biomarkers in earthworms on steel slag samples are analysed in order to find out about the environmental impact of steel slag, and the results indicate that the analysed slag types present no hazard for the environment if used in road construction.

The number and composition of the slag samples were determined using the extreme vertices design method for mixture experiments in order to optimize the experimental work.

Carbonation tests for commercially available steel making slag samples were carried out at different initial CO2 pressures from 1 MPa to 6 MPa, reaction temperatures from 20 °C to 80 °C, and water to slag mixing ratios from 0.25:1 to 3 1.

Copper slag samples were purchased from Mesbareh Company, Kerman, Iran.

The carbon content in these slag samples is higher than the original steel in both cases studied.

SEM investigations of the welding slag samples were conducted in a Hitachi S-3000 H operated at 10 kV (Hitachi, Ltd., Tokyo, Japan).

The adsorption isotherms of the copper slag sample are of type IV and present hysteresis loops of type H2 classification with previous research [21], indicating that the structure is mainly mesoporous with pores having narrow mouths (ink-bottle pores).

The slump flow for the 15% furnace slag sample was within the design value of 550 700 mm.

The free CaO contents of electric furnace oxidizing slag (EOS) samples were found to be below 0.5%.

Fly ash and slag concrete samples were exposed to high temperatures at 400 °C, 600 °C and 800 °C for an hour in a computer controlled, electrically heated kiln.

When taken as a proportion of a single 2 M HNO3 extraction which was applied to slag samples, Cd was the element most readily leached into RSS and control samples.