The increase in pre-reaction results in lower stored energy content for samples consolidated to 400 and 500 °C in comparison to samples consolidated at 25 °C.

Samples consolidated at 300 °C exhibit an abrupt change in temperature response prior to the main ignition temperature.

In contrast, the resulting densities of the SG composite are higher than the CA composite for samples consolidated at 400 and 500 °C.

For samples consolidated at 25 °C, the density of the CA composite is 61.65 ± 1.07% in comparison to 56.41 ± 1.19% for the SG derived composite.

The smallest grain size (d ~ 80 nm) was recorded in MWS samples consolidated at 1400 °C to the density 94.5 %.

The 80-nm grain size TiN samples consolidated by MWS at 1400 °C exhibited well-connected grain boundaries.

The glassy bulk sample consolidated for 600 s at 923 K had a relative density of 99.2%, a saturation magnetization of 46.6 A m2 kg−1, a Curie temperature of 425 K and a low coercivity of 6 A m−1.

Fig. 8 High-resolution image of grain boundary for MWS sample consolidated at 1400 °C.

The smallest grain size (d ~ 80 nm) was observed in the MWS sample consolidated at 1400 °C (Fig. 7a).

This is about two times higher as compared to the average grain size of MWS sample consolidated at the same temperature (Fig. 9).

In addition, those samples were consolidated without significant pre-reaction of the constituents, thus retaining their stored chemical energy.