The pristine raw material was firstly characterized in terms of their proximate and ultimate analyses, following the corresponding technical specifications [14], using a muffle oven (Hobersal model 12PR330CCH).

The sorbent was preliminary heated in a drying oven or a muffle oven during 2.5 h and stored in a desiccator above a saturated solution of H2SO4.

Finally, the coated sample was immersed in boiling water for 10 min, and thermally treated in the muffle oven again at 500°C for 10 min to eliminate the crack defects in the coating.

Finally, NiO/ZnO/SBA-15 nanocomposites were obtained by calcining the dried product at 550 °C for 5 h in a muffle oven at a ramping rate of 1 °C/min.

In brief, 0.2 g samples were processed in a muffle oven at 200 °C for 30 min and then 550 °C for 24 h, and the ash was dissolved in 0.2 mL of concentrated nitric acid.

Recently, Shen et al. reported that the bulk of In2S3 was prepared by In(NO3 3·4.5H2O with H2S at 300 °C for 3 h in the muffle oven [14].

The proximate analysis was performed taking 72 mesh size coal powder using oven and muffle furnace as per Bureau of Indian Standard (BIS 2003).

Weight loss on drying and sulfated ash were determined using a Yiheng vacuum drying oven and muffle furnace, respectively.

Volatile solids were determined by keeping the oven dried sieved sample in a muffle furnace for 550 ± 5 °C for 2 h.

The precipitated titania was then dried in an air oven at 100 ��C and further calcined in a muffle furnace at 400 °C for 4 h.

Ash was determined on the extract after drying in the oven at 105°C, and then samples were transferred in the muffle at 550°C.