Experimental results showed that the DP addition to partially substitute for the pozzolanic materials had no impact on the setting properties of pastes with blended binder of slag and OPC while significantly improved those of the pastes with that of FA and OPC or ternary mixture of slag, FA, and OPC binder.

From these figures, it is observed that the setting times increased when the borax is added to a mixture of slag-lime-plaster of Paris.

A new type of environment friendly polymer-modified waterproof mortar (PMWM) was developed through adding ethylene vinyl acetate (EVA)/vinyl acetate vinyl ester of versatic acid (Va VeoVa) mixture (re-dispersible emulsion powder), mine tailings, quartz sand and additives to the eco-cement, which was prepared by grinding the mixture of steel slag, blast-furnace slag, fly ash and activator.

A mixture of 50% slag 50% SF (cured at 25 and 60 °C) showed no strength loss after the exposure.

The results showed that as the basicity of the mixture of BOF slag and additives decreased, the melting temperature of the mixture decreased, whereas the iron recovery efficiency was significantly improved.

In comparison, a 55% drop of strength was observed in a mixture of 50% slag 50% FA (cured at 25 °C) after the same exposure.

Accordingly, the reactivity index was high, indicating that the residue from the mixture of BOF slag and the additives after recovering iron can be used as an active supplementary cementitious material.

Results show that, the mixture of 40% slag in cement-mortar lining can reduce its initial porosity and Calcium-Silicon ratio, and improve its pore size distribution and phase composition.

For the M3, M4 and M5 mixtures, the incorporation of slag as a ternary blended element did not consume the remaining crystalline silica, as shown in Fig. 9c e.

At this time, hearths could not melt metallic iron, but produced a 'bloom' (a mixture of iron and slag) which could be converted to wrought iron by repeated heating and hammering.

The incorporation of GDS significantly enhanced the compressive strength of the autoclave-cured mixture, whereas the inclusion of slag maintained the compressive strength to be higher or comparable to that of the control mixture.   5.