All the samples were obtained after 10 min of anodization.

A mesoporous layer 100-μm thick was obtained by 60 min of anodization at 14.5 mA/cm².

Sparking occurs sporadically on the surface as the voltage is over 300 V and the instantaneous current density after 45 min of anodization increases with increasing voltage.

The dissolution power of the HF-based electrolyte is evident from Figure 4c, which shows the top surface morphology of the pre-patterned Ti-substrate after 5-10 min of anodization.

The oxide electrode formed after 18 min of anodization shows an energy conversion efficiency of 0.9% with an open circuit voltage of 800 mV and short circuit current of 2.2 mA cm−2.

However, from cross-sectional SEM micrographs, it was seen that after 2 min of anodization, formation of regular nanotubes was observed underneath the non-tubular region similar to that seen in Figure 2.

This is clearly evident from Figure 5c, which shows the top surface morphology of the pre-patterned Ti-substrate after 5-10 min of the second-step anodization in glycerol-based electrolyte.

After another round of anodization for 10 min under the same conditions, followed by immersion in 30%H2O22 solution for 10 min, the anatase TNAs were detached from the Ti substrate.

Based on these results, we concluded that the optimum duration of anodization is 60 min in the present setting because a TiO2 layer showing good photocatalytic activity without any surface cracks could be formed.

Spectral photoresponsivity and PL spectrum (inset) of QDs/PS hybrid-MSM photodetector dependent on anodization times, 5 (i), 10 (ii) and 25 (iii) min, of porous silicon at 16 manodizationzation current.

The effects of applied potential (10 70 V), duration of the third step of anodization (15, 30 and 60 min) and the previous usage of the electrolyte on formation of ATO layers were examined at the anodizing temperature of 40 °C.