The maximum hardness value was measured for WN0.7 (30 GPa).

Maximum hardness value was obtained from Ta-containing coating.

Maximum hardness value according to the various Si concentration is obtained at 32GPa.

The maximum hardness value of DLCM films was 20 GPa while that of DLCA films was 28 GPa.

Then, Genetic Algorithm (GA) was used to find optimum aging time and temperature for the target of maximum hardness value.

The maximum hardness value for this zone was observed near the interface and gradually decreased towards the substrate.

Maximum hardness values linearly increased with increasing implantation dose, from 5.25 to 7.5 GPa.

Maximum hardness values (42 45 GPa) were obtained for the films prepared at CH4/(CH4 + N2) ratios ranging from 0.2 to 0.4.

The maximum hardness values of the Al2O3 films on steel reached 12 GPa and the elastic modulus exceeded 280 GPa.

Samples FS-processed at 1200 rpm, 20 mm/min and three passes exhibited the maximum hardness values between 114.66 and 119.34 VHN.

Maximum hardness values of samples processed with 10, 15, 20 and 25 wt.% borax were 750, 915, 1100 and 1250 HV, respectively.