The pressure-intercept is fixed at 140 GPa, derived from the inflection pressure of SiO2 glass reported by Murakami and Bass (2010).

Our results may suggest that the inflection pressure does not strongly depend on the amount of metal ions because the M/Si (M = Mg, Al) values for SA1 and SA2 are less than for MgSiO3 glass, which has much higher inflection pressure than SA1 and SA2 (Fig. 6).

The pressure conditions at which the increase of dV S /dP occur (hereafter referred to as "the inflection pressure") are 130 ± 5 GPa in SA1 and 116 ± 9 GPa in SA2.

The inflection pressure of SA1 is 10 GPa lower than that of SiO2 glass (Murakami and Bass 2010) and 3 GPa lower than that of MgSiO3 glass (Murakami and Bass 2011).

A novel phenomenon observed in this study was that as pore pressure increased passed an inflection pressure point, nitrogen permeability became directly related to pressure gradient contrary to the trend predicted by Klinkenberg slippage theory.

If we assume that an Al2O3 content of ~13 mol% may possibly be included in partial melts of MORBs generated at around 100 GPa (Pradhan et al. 2015), the inflection pressure is expected to be 124 GPa corresponding to a depth of ~2690 km.

Fig. 6 Inflection pressures in the P-V S profiles of the silicate glasses.

The inflection pressures for SA1 and SA2 are much lower than in MgSiO3 glass, suggesting that Al2O3 promotes the reduction of pressure conditions of inflection caused by an increase of the average Si-O coordination number from 6 to 6+ much more strongly than does MgO.

The sigmoidal equation has four fitting parameters: (a) lower asymptote (volume); (b) distance from lower asymptote to upper asymptote (inspiratory capacity); (c) true inflection point (pressure); and (d) range of pressure from (c) to the point of high compliance.

The numerical simulation indicates that a clear inflection point of pressure gradient may prevail with the presence of internal vertical bifurcation.