For the sake of simplicity of the present study, the total volume of the hydrated paste due to slag hydration was calculated as v h c p, S G = 1.1 × v C S H S (14).

From the study of Chen and Brouwers (2007), it was found that the volume of CSH(S) was approximately 90%% of the total volume of the hydrated paste.

Because not all of the water is used up in the reaction, channels and capillaries of water are left over weaving through the hydrated paste.

The total volume of reacted or hydrated paste, vhcp,FA+SG, at any instant of time was then expressed as the sum of the volume of hydrated paste due to the alkali activation of fly ash and that due to slag hydration.

The hydrated paste containing 80%% slag, 20%% lime and 10%% plaster of Paris was analyzed by XRD (with the testing condition: CuKα; 7° 70°; 2θ; 2° min−1) after different set periods.

Due to the presence of AFt in the hydrated paste, the expansive behaviour resulted in a reduction in the total pore volume by 29 62% (0.01 10 μm), but there were more mesopores (2 50 nm) due to the crystalisation of AFt.

Microstructural and microanalytical characterizations of the hydrated pastes were conducted using a Jeol JSM 6610LV coupled with EDX.

SEM and XRD were used to analyze the microstructure and compositions of hydrated pastes.

The samples for XRD analysis were prepared by grinding pieces of hydrated pastes into a powder form that could pass a 75-μm75-μmsieve

The result of 27Al MAS-NMR spectroscopy indicated the absence of the amorphous AH3 phase in all hydrated pastes.

It is thus unclear how representative this sample is of a product that can actually be found in hydrated pastes, and this questions the validity of the model from Taylor (1986 ▶).