Sentence examples for force of the coating from inspiring English sources

The results showed that the elastic modulus, hardness, and adhesion force of the coating were 408.34 ± 16.25 GPa, 22.56 ± 0.99 GPa, and 33 N, respectively.

Overall, the presence of yttrium, tantalum, and silicon in the coating improved the resistance of high temperature oxidation and enhanced the bonding force of the coating and the alloy.

The effect of the coating on interparticle forces was studied.

The adhesive force of the CNT/metal binder coating on a substrate was measured by a pencil hardness test, which is described in American Society for Testing and Materials (ASTM) D3363.

The imbibition process that we simulate is the result of forcing the coating fluid into the pore space by applying a time-dependent flow-driven pressure distribution to the external surface of the paper, or is driven only by capillary forces.

The adhesion force of ZrO2 coating on α-Fe2O3 is around 100 nN while for the coatings developed on other pre-oxidized surfaces are around 50 nN.

Our analysis indicates that the improvement is attributed to high adhesion force of the smooth and dense coating and the synergistic function of Cr/CrN/Cr multilayer structure.

At intermediate torque values, when the force is high, the width of the coating is high, and its thickness is thin; and when the force is low, the width and thickness are low.

This coat is likely necessary for LB "contraction" and surfactant release into the extracellular space (the term "contraction" denotes an apparent squeezing-out of surfactant through the fusion pore, although contractile forces of this coat have not yet been directly measured).

Cross-cut tape adhesion test manifests that adhesion force of superhydrophobic coating to nitrocellulose lacquer is a highest class of 5B according to ASTM D3359 standard.

But Dr Bruel found that if a hydrogen-treated wafer is first fused to another wafer that has been given a glass coating, the force of the gas bubbles will instead cause a thin silicon film to peel off the one and on to the other.Since the hydrogen-treated wafer is not destroyed by this process, it can be re-used this time as the glass-coated wafere-used this