Two UV curable dielectric materials were deposited and the effects of curing time and curing atmosphere on the inkjet printability of a commercially available silver ink were investigated.
Good wettability of the silver ink was obtained following ozone treatment of the dielectric layers, where the treatment required was found to be a function of the dielectric formulation and the curing atmosphere.
A research program was carried out to investigate the effects of duration of initial steam curing at atmosphere pressure on compressive strength of concrete with low water/binder ratio.
All concrete specimens were either water cured or atmosphere (Air curing) cured with relative humidity of 60% and 20 °C for 28 days.
It was demonstrated that the thin films fabricated by spin-coating the ITO nanoparticle coating solutions on glass substrates followed by 413.15 K heat curing under nitrogen atmosphere for 30 min were transparent conductive ITO thin films with a sheet resistance of 1.9 × 105 Ω/□.
Foams with an open-cell structure are produced by incorporating an inert gas into the resin under pressure and then releasing the mixture to the atmosphere and curing the resulting foam.
Atmosphere cured concretes show greater variation in air permeability and Da for all W/B than water cured concretes suggesting that the pore structure can alter the chloride transport in concrete.
In the case of atmosphere cured concrete subjected to vacuum during air permeability test and later saturated when subjected to electrophoretic test changes the internal conditions of concrete; from dry concrete including unreacted cement to saturated concrete with possible rehydration reaction.
In case of laboratory prepared atmosphere cured concrete, low correlation was observed between air permeability and De due to the changes in pore structure of concrete when concrete is transferred from air permeability test to electrophoretic test because of possible rehydration reaction of cement in the process of electrophoretic test of chloride ion and saturated water processing.
Regardless of cement types used, air permeability is lesser for water cured specimens than atmosphere cured similar to other findings (Mu et al. 2015).