b Cracking at the end of constant current corrosion process.

A constant current accelerated corrosion test was performed on five fiber optic corrosion sensors and the relationship between reflected wavelength change from the grating and the weight loss rate of rebar was obtained by the gravimetric weight loss method.

The test results generated show that accelerated corrosion using impressed constant current produces more corrosion damage than that using constant voltage.

In this paper, an experimental program is designed to study which of the two accelerated corrosion techniques (using constant voltage and constant current) produces more corrosion damage for similar amount of induced corrosion level (steel loss).

However, no studies could be found which had considered the effectiveness of the using constant voltage technique versus the constant current technique in simulating corrosion damage in reinforced concrete.

Hence, it can be concluded that accelerated corrosion using constant current is recommended over the constant voltage in studying the effectiveness of various materials, repair strategies and admixtures to resist corrosion damage.

Therefore, it can be concluded that accelerated corrosion using constant current also produces greater structural damage to the concrete columns than using constant potential.

Therefore, it can be concluded that accelerated corrosion using constant current also produces greater structural damage to the concrete columns than using constant potential.  .

Two concrete columns (labeled C3 and C4) were subjected to accelerated corrosion using constant voltage and two other concrete columns (labeled C5 and C6) were subjected to accelerated corrosion using constant current.

The experimental setup for accelerated corrosion under constant current is similar to that used for constant voltage except that the power supply is replaced by a constant current power supply.

Using accelerated corrosion through the application of a constant current of one ampere, four levels of corrosion were established at 5%, 10 %, 15, and 20% of mand loss of the reinforcing bars.