A difference in the blackening of the silver coatings between the two codices is visible, too (Computer Vision Lab (CVL), Vienna University of Technology, DI Fabian Hollaus).

Titanium alloys (e.g., Ti-6Al-4V) are typically used in the interfacial porous coatings between the implant and the surrounding bone to promote stability.

Potentiodynamic polarization results revealed the corrosion current density (icorr) values obtained for both coatings (between 0.6 and 0.85 μA/cm2) were lower than bare specimen (1.2 μA/cm2).

A comparison of the authigenic clay mineral coatings between the sample sets of the Heron, Egret, Seagull and Skua fields (Fig. 1b) shows a lower fraction of coated grains and lower surface coverage rates for the Seagull sample sets (Fig. 13).

Coatings between 2 and 10 μm were prepared by using concentrated and diluted sols by dipping and EPD process and the corrosion behaviour of the coated substrates were studied through potentiodynamic and impedance spectroscopy measurements (EIS).

Measurements of the concentrations of SiH groups (using the characteristic vibration at 2160 cm−1) were obtained from coatings between 1 and 27 μm in thickness, over temperatures ranging from 25 to 120 °C.

The results show that the solar absorbance of these coatings is between 0.82 and 0.94, the thermal emittance is between 0.05 and 0.27, and the brightness is in the range of 0.65 8.89%.

It is seen that the highest alteration in electroactive surface area for all deposited coatings is between deposition times of 60 and 120 s.

Uniform composite coatings containing between 20 and 70 wt.% of PEEK have been obtained.

The size of nanocrystalline grains in the Mo coatings ranged between 2 nm and 10 nm.

The magnesium content in the coatings varied between 1 at.% and 60 at.%.