Sentence examples for chemical conversion coating from inspiring English sources
Unfortunately, the protective abilities of various chemical conversion coating candidates, i.e. phosphate coating, rare earth conversion coating and permanganate/vanadate/tungstate conversion coatings, are still inferior to CCCs due to the lack of critical self-healing functionality.
A self-designed wax deposition apparatus based on cold-finger was used to study the wax-repellent properties of coatings, which indicated that all chemical conversion coatings showed superior wax-repellent performance to bare carbon substrate and the wax deposition reduction value of 80 95% was achieved by the chemical conversion coating obtained at room temperature.
Environmentally friendly chemical conversion coating based on permanganate phosphate solution was used in this study.
In this paper, a simple vanadia based chemical conversion coating was applied for improving the corrosion resistance of high strength AA2024 alloy.
The designing idea for the chemical conversion coating with high corrosion resistance (CR) and low electrical contact resistance (ECR) on AZ91D Mg alloy was presented.
Barium phosphate chemical conversion coating is a new research area for the corrosion protection of Mg alloys.
The deposition of stannate chemical conversion coatings on AZ91 D magnesium alloy by using the potentiostatic technique was investigated to improve uniformity and corrosion protection performance of the coating film.
In this work, CeO2/stannate multilayer coatings on AZ91D magnesium alloy were successfully obtained by chemical conversion and sol gel dip coating.
The parameters of the chromate bath, like temperature, pH, and fluoride content, strongly affect the morphology and chemical composition of the chromate conversion coating and as a consequence have a large influence on its corrosion performance.
Effects of the immersion time, pH value and solution temperature on the corrosion resistance and the chemical composition of the titanium conversion coating were investigated by the salt spray test (SST) and XPS, respectively.
Two-step chemical conversion process was used to coat MgF2 on the surface of ZK60 alloy.