The distance between source and substrate was fixed at 23 cm.

Since both the ZnO nanorods samples were prepared under the same condition in the furnace including the source temperature, the distance between source and substrate and Ar flow; it can be concluded that the crystal quality is a key factor influencing the orientation and the crystal quality of the above ZnO nanorod arrays.

The distance between sources and substrates was around 5 mm, and the growth surface was a circle of 7 mm of diameter.

The dependence of nanowire diameter on separation distances between metal source and substrate has been studied.

Various experimental conditions such as separation distance between metal source and substrate, growth temperature, gases flow rates, and catalyst nanoparticle sizes are shown.

The separation distance between metal source and substrate controls the nanowire diameter on the basis of boundary layer thickness and reactant vapor species.

Diameter of root grown ( beta )-Ga2O3 nanowires having monoclinic crystal structure is tuned by varying separation distance between metal source and substrate.

Top panel of schematic shows that the nanowire diameter decreases with increase in separation distance between metal source and substrate as reactant vapor species depleted downstream and boundary layer thickness increases.

Ga2O3 nanowires grown at 900 °C for 30 min using 50 nm Au nanoparticles as catalyst with total gas flow rates of 80mL/minn (Ar/O2 3/1) have been studied using different separation distances (S d ) between metal source and substrate (Fig. 2).

The impact of an argon/hydrogen microwave plasma treatment on silicon and silicon dioxide is investigated as a function of temperature as well as distance between plasma source and substrate.

We have demonstrated an evaporation method to obtain a uniform organic thin-films with designed evaporation source which have array of two dimensional apertures of different sizes above an evaporation source optimized the distance between evaporation source and substrate, a uniform film was formed.