Sentence examples for applied under tension from inspiring English sources

The composite bow's resistance to bending was increased by reinforcing the rear, or belly, of the bow with horn; its speed and power in recoil were increased by overlaying the front of the bow with sinew, usually applied under tension.

He applied under the 'faint hope' clause.

We numerically investigate the elastic deformation response of a two-phase soft composite under externally applied concentric tension.

Here we employ molecular dynamics simulation to explore the behavior of a graphene aerogel-inspired superstructure under applied compression and tension with a focus on the mechanical stabilizing mechanisms and properties of the deformed structures.

Under different rubrics dirty hands, applied ethics the tension persisted.

The first cyZD treatment was carried out at a drawing temperature of 90°C under an applied tension of 8.7 MPa, the second at 90°C under 209 MPa, and third at 130°C under 366 MPa.

The CZD treatment was carried out at a drawing rate of 420 mm/min and in three steps; the first CZD (CZD-1) at a drawing temperature of 210°C under an applied tension of 30.3 MPa, the second (CZD-2) at 220°C under 229.5 MPa, and the third (CZD-3) at 230°C under 364.9 MPa.

To orient amorphous chains selectively, two HTA treatments were carried out; the first HTA (HTA1) at 100°C under an applied tension of 143.3 MPa, and the second (HTA2) treatment at 110°C under 142.0 MPa.

Lattice strains under externally applied tension and compression in all three phases of the composite were measured using energy dispersive synchrotron X-ray diffraction.

The zone-drawing was carried out at a drawing temperature of 130°C under an applied tension of 13 MPa, and the zone-annealing was carried out at an annealing temperature of 200°C under 212 MPa.

The obtained NFMF was annealed at 85 °C under an applied tension of 5.14 MPa to improve the mechanical properties; the annealed NFMF had a Young's modulus of 2.1 GPa and a tensile strength of 68 MPa.