Sentence examples for a crack width of from inspiring English sources

The obtained test results reveal that for the girders with higher fibre dosages the shear load can be increased with 78% before reaching a crack width of 2.5 mm.

For a crack width of 0.09 mm, the corrosion initiation period was about 14 days.

For Class 1 exposure (moderate exposure), the equation is calibrated, through γ d  = 1, for a crack width of 0.43 mm (0.017 in).; for Class 2 exposure (severe exposure), γ d  = 0.75.

The stresses at two different characteristic points (at w 0.3 and w 1%) are expressed as follows: f_{bt} = frac{{fleft( {w_{0.3} } right)}}{{Kgamma_{bf} }} (8) f_{1% } = frac{{fleft( {w_{1% } } right)}}{{Kgamma_{bf} }} (9 where f bt is the stress at a crack width of 0.3 mm and f 1% is the stress at a crack width corresponding to 0.01H.

The experiments show significant results: an excellent improvement in the loading capacity of around 170% and a crack width reduction of around 58%. FEM analysis results using ABAQUS software showed excellent agreement with experimental results.

Additionally, the reduction ratio of the flow rate for the specimens with a crack width range of 0.24 0.36 mm corresponds to 0.343 0.519, 0.524 0.716, and 0.631 0.826 in specimens S-0.5, S-1.0, and S-1.5, respectively.

At the age of 28 days, specimens were pre-cracked to introduce a surface crack width of between 100 and 400 μm.

It was found that the rutting depth in all specimens after 1 h (2400 wheel passes) at 45 °C was smaller than 1 mm, but that the tensile strains in all specimens at 1 hour were 25,000 × 10−6 (2.5%) or larger and a strain of 3.69% which corresponds to a longitudinal crack width of 0.555 mm by CT analysis and ARAMIS system.

a Shear crack width of 0.3 mm.

There is evidence that a threshold crack width of about 0.05 mm exists for water permeability.

Beam B2 experienced failure in shear at 124 kN, with a maximum crack width of 3.31 mm.